reprap-industrial-v1:knowledge-base [2016/01/25 13:17] Markus Bürgener [Polylactic Acid (PLA)] |
reprap-industrial-v1:knowledge-base [2016/01/25 13:54] Markus Bürgener [Polylactic Acid (PLA)] |
||
|---|---|---|---|
| Line 1149: | Line 1149: | ||
| | Build chamber temperature | OFF°C | [[{|width: 8em}#adjusting-the-build-chamber-temperature|Build chamber temperature]] | | | Build chamber temperature | OFF°C | [[{|width: 8em}#adjusting-the-build-chamber-temperature|Build chamber temperature]] | | ||
| | Extruder temperature | 180-220°C * | | | | Extruder temperature | 180-220°C * | | | ||
| - | | Speed settings | standard settings for ABS; for filled materials, reduce speed * | | | + | | Speed settings | reduce standard settings for ABS by 20% *\\ Perimeters: 20mm/s\\ Infill: 24mm/s | | |
| | Idler lever preload | 4.0mm | [[{|width: 8em}reprap-industrial-v1:service-guide#extruder-idler-lever|Setting the idler lever preload]] | | | Idler lever preload | 4.0mm | [[{|width: 8em}reprap-industrial-v1:service-guide#extruder-idler-lever|Setting the idler lever preload]] | | ||
| | Nozzle tip | all | | | | Nozzle tip | all | | | ||